| Specification | : | Resin 6 Kg Pack |
|---|---|---|
| Appearance Liquid | : | Natural |
| Specific gravity @ 25°C | : | 1.45 |
| Viscosity @ 25°C, poises | : | 12000-15000 |
| Colour | : | Off White |
| Amine value by HCIO4 method Mg of KOH/gm | : | 450 |
| Mixing Ratio: Epoxy Compound: Hardener | : | 6Kg : 1Kg |
| Working Timing | : | 10 to 15 minutes |
| Hardener after 8 hrs. | : | Shore D-40 |
| Tensile Strength Kgs/cm2 | : | 250-300Kgs/cm2 - 90MPA |
| Compressive Strength | : | Min 600Kgs/cm2 - 0.48 GPA |
| Hardener's Specification | ||
| Solids | : | 95 Min |
| Viscosity (cPs, @ 25 deg C) | : | 500 ~ 1500 |
| Colour | : | Orange-Brown |
| Amine Value (mg KOH/g) | : | 360-420 |
| Density (g/ml@25 deg C) | : | 0.99 ~ 1.05 |
| AHEW | : | 95 |
| Flash Point (deg C) | : | >104 |
| Gel Time (mins, 100gm @ 25 deg C) | : | 20-30 |
| PHR* 0 for EEW-190 | : | 50±5 |
| Deg C | : | 3-4hrs. |
| Fully Cured | : | 7 Days |
| Cross hatch | : | 5B |
| Pencil Hardness | : | <4H |
| Chemicals Resistance | : | Resist to mild acid and base Poor resistance to solvent |
| Compressive Strength (mPas.) | : | >60 mPass |
Hardener is soulable in aromatic hydrocarbons, higher alchols, ketones and insoluble in aliphatic hydrocarbons and water. Grouting materials are selected based on the type of load they will support. Dynamic loads are associated with reciprocating equipment, motor, generators, turbines etc. Static loads are associated with columns or non-moving equipment. Epoxy grouts offer unique performance advantages in many applications. They achieve quickly, allowing fast return to service or commissioning of equipment. Greater bond to the underside of prepped baseplate, density and lower modulus of elasticity help to absorb impact and vibration. Low shirnkage and high tensile and flexural strengths optimize load transfer ensuring stable, secure alignment and protecting equipment from unnecessary wear and tear, Chemical resistance properties ensure they are durable even in harsh industrial enviroments. With more than 25 years of experiance in precision equipment grouting. HANDA CHEM is an early developer and pioneer in both cementitous and epoxy grouts. We understand not only the in-service performance demands that our grouts must meet, but also the inter-relationship between various physical properties and application criteria that must be carefully considered. Handa Chem has applied advanced chemistry to balance the physical properties of compressive strength, bearing area, chemical and high temperature resistance, shirnkage and creep with the sometimes difficult yet also very important application enablers of flow and working time, to provide uncompromised and durable support, protecting the equipment investment by improving reliability, operating efficiency and life cycle of machinery . The performance of any epoxy grout, in fact for most all construction materials depends on the proper fit-for-purpose design, and the proper installation. This Guide to Epoxy Grouting is designed to help equipment manufacturers, engineers and specifiers, owners and contractors understand the proper preparation, Mixing, Installation & Testing of Epoxy Grouts to enable durable, quality, installation of Grouts.
Hardener is compatible with all grades of modified and unmodified liquid Resins and Epoxy compound the curing is dependent on the hardener system and tempreature for technical department of the company.
Parts by Weight
This 7 kg pack is specially made for Road safety
| Specification | ||
|---|---|---|
| Appearance Liquid | : | Natural |
| Specific gravity @ 25°C | : | 1.45 |
| Viscosity @ 25°C, poises | : | 12000-15000 |
| Colour | : | Off White |
| Amine value by HCIO4 method Mg of KOH/gm | : | 450 |
| Mixing Ratio with 6 Parts of Epoxy | : | 1KG Hardener |
| (a) 1KG Resin (b) 166 GMS Hardener | ||
| Pot Life of 140gm | : | 8 to 10 minutes |
| Epoxy Compound 6Kg | : | Hardener 1 KG |
| Tensile Strength Kgs/cm2 | : | 90MPA |
| Compressive Strength | : | 0.48 GPA |
Hardener is soluble in aromatic hydrocarbons, higher alcohols, and ketones and insoluble in aliphatic hydrocarbons and water.
Parts by Weight
Hardener is compatible with all grades of modified and unmodified liquid Resins and Epoxy compound the curing is dependent on the hardener system and tempreature for technical department of the company.